Texture Analysis of Inconel 718 with Different Modes During Single Track Laser Surface Re Melting

Author(s)

Abstract

An in-depth understanding of the texture formation in melt pools allows for the modification of the surface layer microstructure and corresponding material properties, providing an opportunity to integrate laser surface re-melting into metal additive manufacturing. This study investigates crystallographic texture formation at different cooling rates in single melting tracks on the Inconel 718 (IN718) plate produced by laser surface re-melting. The cooling rate varies from 2.31 × 105 °C/s to 9.56 × 105 °C/s with the increase in scanning rates from 400 mm/s to 1200 mm/s, measured by recently developed real-time temperature monitoring of melt pools. Columnar grains are dominant, with distinct crystallographic textures forming in the melt pools. At a slower scanning speed, the keyhole mode shows three different textures forming at different depths (crystallographically layered structure), while, at a faster scanning speed, the conduction mode shows only random grain orientation. There are no pores/voids detected, and the columnar grain morphology and columnar grain width (8.6 μm to 12.4 μm) follow the analysis framework in terms of thermal gradient and solidification rate analysis. This implies that laser surface re-melting provides the potential to modify the surface structure from a random grain orientation to a crystallographically layered structure.

Download Paper

Keywords

Additive manufacturing

Citation

Issues

If you have any questions about this publication or are having problems accessing it, please contact [email protected].